Chemical Composition (%): Similar Brand Inconel 718 Physical Property Mechenical Property(Min) Tensil Strength Rm  N/mm2 Yield Strength RP0.2N/mm2 Elongation A5% Features Processing Hot working Proper working temperature 1120-900ºC,cooling method is water quenching or other quick cooling method. It must be annealing in time after hot working to maintain best properties. The material should be heat to processing temperature limited when hot working, in order to ensure the material plasticity during processing, when the deformation reaches 20% the final processing temperature should not be lower than 960 ºC. Cold working Cold working should be after solution annealing,the rate of hard working is greater than austenitic stainless steel, therefore the equipments need to be adjusted,and there should be solution annealing process during cold processing. 1 Q: What's the payment term? A: T/T 30% for down payment, Then T/T balance on the actual weight of ready for shipment products on the basis of the Seller's account. 2 Q: How to ensure your products is qualified? A: The Quantity and weight of product are certified by the seller's Inspection Certificate and the quality is certified by the Mill Taste Certificate agreed form. 3 Q: How to confirm the Acceptance of Goods and Quality Control? A: Once the manufacturing of a batch is complete, two samples will be acquired at random by the buyer's representatives for testing at independent labs. One sample will be sent to a lab in Seller's country and the other sample to a lab in buyer's country. Antiqued Roof Materials,Antique Tile,Roof Ridge Strip Palindromic Head,Ancient Architecture Sugarcane Ridge Huaxian Tangyu Garden Landscape Engineering Co., Ltd. , https://www.carvedbricks.com
Element
Min
Max
C
-
0.08
Mn
-
0.35
Si
-
0.35
P
-
0.015
S
-
0.015
Ni+Co
50.0
55.0
Cr
17.0
21.0
Co
-
1.0
Fe
Bal
Al
0.35
0.80
Mo
2.80
3.30
Ti
0.65
1.15
B
0.001
0.006
Cu
-
0.15
Nb+Ta
4.75
5.50
GB/T
UNS
Trademark
JIS
ISO
GH4169
N07718
Inconel718
NCF718
NiCr19Nb5Mo3
Density
8.22g/cm3
Melting Point
1260-1340ºC
Alloy
HB
Solution Treatment
965
550
30
≤363
Packing: In wooden case.
Delivery: About 45days after receiving the down payment.
Company Information
Our company is specialized in making high quality high speed steels, M2, M35, M42, W9, W18 and some mould steels , maraging steels,nikel bars etc. Our products have exported to many countries like Russia, Germany, Netherlands, Hungary, Vietnam, Italy etc. and we received many good feedback.Â
If you are interested in our products, please send us inquiries and contact us freely, hope we can get a further cooperation!
  
 Â
FAQ
How To Contact Us
Â
Model NO.: Inconel 718
Elogation: 35%
Ultimate Strength: 1170MPa
Surface: Peeled or Bright
Tolerance: 0/+0.5mm(as Your Request)
Delivery: Solution Annealing
Certificate: Mill Test Certificate
Trademark: DLDT
Transport Package: in Wooden Case
Specification: dia3mm
Origin: China
Alloy 718 is a precipitation hardenable nickel-based alloy designed to display exceptionally high yield, tensile and creep-rupture properties at temperatures up to 1300°F. The sluggish age-hardening response of alloy 718 permits annealing and welding without spontaneous hardening during heating and cooling. This alloy has excellent weldability when compared to the nickel-base superalloys hardened by aluminum and titanium. This alloy has been used for jet engine and high-speed airframe parts such as wheels, buckets, spacers, and high temperature bolts and fasteners.